K0305 (Formerly Coded K0411)
             
Chromaticity and NVIS Radiance
Source u' v' x y Y (%) N/R A
1600 K 0.162 0.553 0.353 0.536 25.6 1.2E-09
1700 K 0.156 0.550 0.340 0.530 27.1 1.1E-09
1800 K 0.152 0.546 0.328 0.524 28.5 1.0E-09
1900 K 0.148 0.543 0.317 0.516 29.7 9.1E-10
2000 K 0.145 0.539 0.307 0.508 30.9 8.4E-10
2100 K 0.142 0.535 0.298 0.500 31.9 7.8E-10
2200 K 0.139 0.532 0.290 0.491 32.9 7.2E-10
Physical Properties
Nominal Thickness 2.00 mm
Refractive Index nD = 1.641
Density 3.61 g/cc
Thermal Linear Expansion 97E-7 /oC
Transition Temperature 513 oC
Annealing Temperature 525 oC
Deformation Temperature 542 oC
             
Wavelength Transmittance Wavelength Transmittance Wavelength Transmittance
(nm) (nm) (nm)
300 0.00000 515 0.78849 730 0.00000
305 0.00000 520 0.77211 735 0.00000
310 0.00000 525 0.75348 740 0.00000
315 0.00000 530 0.73678 745 0.00000
320 0.00000 535 0.70229 750 0.00000
325 0.00000 540 0.66840 755 0.00000
330 0.00000 545 0.62926 760 0.00000
335 0.00000 550 0.58144 765 0.00000
340 0.00000 555 0.53922 770 0.00000
345 0.00000 560 0.48157 775 0.00000
350 0.00011 565 0.42880 780 0.00000
355 0.00160 570 0.37163 785 0.00000
360 0.01030 575 0.31922 790 0.00000
365 0.03515 580 0.26436 795 0.00000
370 0.08401 585 0.21826 800 0.00000
375 0.15185 590 0.17257 805 0.00000
380 0.22908 595 0.13685 810 0.00000
385 0.30899 600 0.10437 815 0.00000
390 0.38462 605 0.07837 820 0.00000
395 0.44368 610 0.05705 825 0.00000
400 0.50079 615 0.04099 830 0.00000
405 0.54941 620 0.02882 835 0.00000
410 0.58191 625 0.01952 840 0.00000
415 0.61184 630 0.01306 845 0.00000
420 0.63342 635 0.00864 850 0.00000
425 0.66560 640 0.00547 855 0.00000
430 0.67657 645 0.00348 860 0.00000
435 0.69626 650 0.00215 865 0.00000
440 0.71526 655 0.00132 870 0.00000
445 0.72650 660 0.00079 875 0.00000
450 0.74032 665 0.00047 880 0.00000
455 0.75238 670 0.00027 885 0.00000
460 0.75873 675 0.00016 890 0.00000
465 0.76624 680 0.00009 895 0.00000
470 0.77943 685 0.00005 900 0.00000
475 0.78112 690 0.00003 905 0.00000
480 0.79077 695 0.00002 910 0.00000
485 0.79935 700 0.00001 915 0.00000
490 0.80021 705 0.00001 920 0.00000
495 0.80800 710 0.00000 925 0.00000
500 0.80280 715 0.00000 930 0.00000
505 0.80136 720 0.00000
510 0.79620 725 0.00000